Paint & Constructions

ProductTypeVisocityPHDownload Link
AOPL C 76WATERPROOFING ACRYLIC EMULSION- 8.5-9.5Click to Download
AOPL –C400FLEXIBLE CEMENTITIOUS EMULSION 1700 - 3000 cP7.0-8.5Click to Download
AOPL – EM 50Polyvinyl Acetate Dispersion50000 – 70000 cP5.0-6.0Click to Download
AOPL MURA C 55ACRYLIC BINDER FOR ELASTOMERIC ROOF COATING AND MASONRY COATINGS1000 cP max7.5-8.5Click to Download
AOPL PA 561Pure Acrylic 50%400 – 500 cP8 ~ 10Click to Download
AOPL P DEFSilicone Defoamer6000 – 8000 cP5.5 ~ 7 poise (approx.)Click to Download
AOPL P DISDispersing Agent120 – 150 cP7.5 ~ Click to Download
AOPL PS 259Styrene Acrylic 48%1500 – 2000 cP8 ~ 10Click to Download
AOPL PS 504Styrene Acrylic 50%6000 - 8000 cP8 ~ 9Click to Download
AOPL PS 3045Styrene Acrylic 45%1500 – 2000 cP8 ~ 10Click to Download
AOPL PVB 55Vam Acrylate Copolymer3500 – 4500 cP4 - 5Click to Download
AOPL PVV 50VAM VEOVA ter polymer emulsion2000 - 3000 cP6.0-7.0Click to Download
AOPL PVV 55VAM VEOVA TER POLYMER 55 %3000 - 4000 cP4 - 6Click to Download
AOPL PT 29ALKALI SWELLABLE ACRYLIC THICKENER2000 cP Minimum2– 4Click to Download
Note: The above information is to the best of our knowledge true and accurate. Since the conditions that the products are used in cannot be handled or controlled by us we cannot guarantee the results and assume liability to damages incurred by using this product Refer to M.S.D.S. for handling procedures.

AOPL C 76 WATERPROOFING ACRYLIC EMULSION

AOPL-76 IS A MODIFIED ACRYLIC POLYMERDESIGNED FOR CEMENTITIOUS COMPOSITIONS AN EXCELLENT WATER PROOFING CHEMICAL.
• COMPARED WITH UNMODIFIED CEMENT MORTARS AOPL-76 MODIFIED MORTARS HAVE BETTER FLXURAL,COMPRESSIVE AND IMPACT STRENGTH BESIDES EXCELLENT ABRASION RESISTANCE.

• AOPL-76 IS WIDELY USED FOR WATERPROOFING OF TERRACES,ROOFTOPS,BASEMENTS AND CRACKFILLING.

• AOPL-76 EXHIBITS EXCELLENT ADHESION TO CONCRETE,MASONRY,BRICK,WOOD,METALS,ETC. WHEN USED WITH WHITE CEMENT.

• THIS UNIQUE CHEMICAL IS RESISTANT TO HEAT,UV AND CHEMICALS.

SPECIFICATIONS :

APPEARANCE : WHITE MILKY LIQUID
SOLIDS : 45-47%
pH : 8.5-9.5
SPECIFIC GRAVITY : 1.03-1.05
FREEZE THAW STABILITY : 5 CYCLES
FORMULATION TECHNIQUES :

1. FOR CEMENTITIOUS COMPOSITIONS
BLEND 10 PARTS OF AOPL-76 WITH 100 PARTS OF WATER AND THEN ADD A PREBLEND OF SILICIOUS SAND-200 PARTS AND CEMENT 100 PARTS SLOWLY WITH STIRRING AND GET CONSISTENCY AS DESIRED BY ADDING EXTRA WATER IF REQUIRED. THIS SHOULD BE APPLIED ON PRECLEANED SURFACES AND STANDARD CURING PROCEDURE TO BE USED.

2. FOR WATER PROOFING
MIX 2.5 KG OF AOPL-76 WITH 2.5 KG WATERAND SLOWLY ADD 50 KG WHITE CEMENT AND MIX WELL FOR ADDITIONAL PROTECTION FROM WATER SEEPAGE ONE CAN MAKE A UNIFORM FILM OF AOPL-76 ON THE SURFACE BEFORE APPLYING THE MIXTURE OF AOPL-76 AND WHITE CEMENT.

3. FOR EXTERIOR PAINT
USE ABOUT 5% OF THE TOTAL PAINT THE AOPL-76, THIS WILL GIVE A FASTDRYING CLEAR GLOSSY EXTERIORS.

AOPL –C400 FLEXIBLE CEMENTITIOUS EMULSION

AOPL-C400 IS A MODIFIED ACRYLIC POLYMER DESIGNED FOR CEMENTITIOUS COMPOSITIONS AN EXCELLENT WATERPROOFING CHEMICAL.
• COMPARED WITH UNMODIFIED CEMENT MORTARS AOPL-C400 MODIFIED CEMENT MORTARS HAVE BETTER FLEXURAL, COMPRESSIVE AND IMPACT STRENGTH BESIDES EXCELLENT ABRASION RESISTANCE.

• AOPL-C400 IS WIDELY USED FOR WATERPROOFING OF VERTICAL SURFACES WHERE CRACKS OCCUR DUE TO THERMAL EXPANSION AND CONTRACTIONS.

• AOPL-C400 EXHIBITS EXCELLENT ADHESION TO CONCRETE, MASONRY, BRICK, WOOD, METALS ETC WHEN USED WITH WHITE CEMENT.

• EXCELLENT BARRIER COATING AND ALSO FINDS SUITABILITY AS TILE ADHESIVE

SPECIFICATIONS:

VISUAL APPEARANCE : WHITE MILKY EMULSION

SOLIDS : 53-55%

VISCOSITY
RVT SPLINDER NO 4 : 1700 - 3000 cP

SPEED 10 RMP

pH : 7.0-8.5

GLASS TRANSITION TEMP (CALC) : -5 DEG C

FREEZE THAW STABILITY : 5 CYCLES

FILM PROPERTIES : HIGHLY TACKY, FLEXIBLE, CLEAR

AOPL – EM 50 Polyvinyl Acetate Dispersion

Type : Vinyl acetate homopolymer

Visual Appearance : White Dispersion

Solids : 48-50%

Viscosity @ 30ºCby
Brookfield RVT : 50000 – 70000 cP

Spindale No 7 RPM 20

pH : 5.0-6.0

MFFT : 14 deg c

Film : Clear hard film, free from bits

AOPL EM 50 can be used for low cost semi gloss paint applications for interior paint applications and also for cementitious substrates.

AOPL MURA C 55 ACRYLIC BINDER FOR ELASTOMERIC ROOF COATING AND MASONRY COATINGS

AOPL MURA55 is a new generation Acrylic copolymer dispersion, Apeo free and formaldehyde freedesigned for high performance elastomeric coating on roofings.

AOPL MURA55 latex is developed as a high performing, high tensile strength polymer that, when formulated into a Elastomeric Roof Coating formulation, delivers improved toughness and hail resistance Coatings ,with excellent adhesion to polyurethane foam and a variety of other construction and roofing substrates.

TYPICAL DATA:

Total Solids : 55.0-57.0

PH : 7.5-8.5

Viscosity @ 23 0C : 1000 cP max
Brookfield RVT
Spindale No 7
RPM 20

TYPICAL PROPERTIES:

Particle Size, microns : 0.3-0.5

MFFT 0C, approx : 0

Glass Transition Temperature (ONSET) : -35 0C

Specific Gravity Dispersion : 1.03-1.04

Features

100% acrylic composition -------- Outstanding exterior durability

Dirt-resistant chemistry -------- Maintains attractive appearance

Low glass transition temperature -------- maintains flexibility and bridge cracks

Permeable to water vapor -------- Permits water vapor in substrate to escape

Ultraviolet resistance -------- Improves chalk resistance and tint retention

Permanently flexible -------- eliminates the need for external plasticizer

Waterborne -------- Simple handling and cleaning

Application guidelines for using

Formulation– Masonry Restoration Paint (40% PVC)

Material Name : KG

Natrosol 250 MR (3.0%) : 100.0

Water : 50.0

Dispersing agent (30.0%) : 7.0

KTPP (100.0%) : 1.0

Propylene Glycol : 23.9

Nonionic emulsifier : 4.0

Preservative : 1.6

Nopco NXZ : 2.0

fungicide : 6.5

Ti-Pure R-706 : 200.0

Duramite : 250.0

Grind for approximately 15 minutes then letdown with minimum agitation. Before letdown, reduce to slow speed and add the AOPL MURA55 polymer. Continue agitation at a low speed while adding the other ingredients. Upon completion of all additions, reposition the impeller to maintain a good vortex. Mix for 5 minutes.

AOPL MURA55 : 400

Texanol : 6

Nopco NXZ : 2

Aqueous Ammonia (28%) : 2

Natrosol 250 MR (3.0%) : 115

Total : 1170

PVC : 40.1

Volume Solids : 40.9

Weight Solids : 56.9

VOC, g/l : 83

Formulation– ELASTOMERIC WALL COATING (35% PVC)

Material Name : KG

Natrosol 250 MHR (2.5%) : 108.0

Dispersing agent (30.0%) : 5.0

Propylene Glycol : 19.0

Nonionic emulsifier : 4.5

Preservative : 1.5

Nopco NXZ : 3.6

Fungicide : 6.5

Ti-Pure R-960 : 100

Duramite : 325

Grind for approximately 15 minutes then letdown with minimum agitation. Before letdown, reduce to slowspeed and add the AOPL MURA 55 polymer. Continue agitation at a low speed while adding the otheringredients. Upon completion of all additions, reposition the impeller to maintain a good vortex. Mix for 5 minutes

AOPL MURA55 : 528

Texanol : 6.0

Nopco NXZ : 3.0

Aqueous Ammonia (28%) : 1.0

Natrosol 250 MR (3.0%) : 18.5

Thickener : 2.0

Water : 2.0

Totals : 1134

PVC : 35.1

Volume Solids : 50

Weight Solids : 63

VOC, g/l : 56

HEALTH & SAFETY:

Please refer to the Material Safety Data Sheet for safety and environmental information. AOPL MURA55 is not classified as dangerous .

STORAGE & HANDLING:

Store at an even temperature of between +5 0C and +32 0C avoiding frost and direct sunlight. Stir product before use. If stored according to these conditions and in the original unopened containers, the dispersion will be stable for 6 months .

AOPL PA 561 Pure Acrylic 50%

Chemical type : Pure Acrylic

Visual Appearance : Milky white

Solid content : 50 +/- 1%

Viscosity @ 30 C
Brookfield RVT : 400 – 500 cP
Spindale No 4
RPM 10

pH : 8 ~ 10

Free monomer content : < 0.3%

MFFT : 18°C

Properties : Surfactant stabilized fine particle size, excellent binding, good wet scrub, excellent color retention. UV resistant & low dirt pick-up.

Recommended Applications : For use in high sheen/high gloss, premier quality interior/exterior paint.

AOPL P DEF Silicone Defoamer

Chemical Type : Defoamer

Visual Appearance : Thick White Emulsion

Chemical Composition : Dimethyl Polysiloxane

Viscosity @ 30 C
Brookfield RVT : 6000 – 8000 cP
Spindale No 4
RPM 10

pH at 2% : 5.5 ~ 7 poise (approx.)

Suitable Dilutants : Soft water

Defoaming : 9 sec. (approx.)

Uses of Defoamer : Textile Industry

Paper Industry, Dye Manufacturing Industry, Laundries, Paint Industry, Effluent Treatment Plants

Recommendations : It is advisable to add AOPL DEF to any bath before agitation

AOPL P DIS Dispersing Agent

Chemical type : Disperser

Visual Appearance : Water white

Solid content @ 120 °C for 2 hours : 39% - 41%

Viscosity @ 30 C, on BF-RVT (SP-4, 10 RPM) : 120 – 150 cP

pH : 7.5 ~ 9

Diluents : Water

Uses of dispersant : AOPL DIS is a pigment dispersant for aqueous systems. It is a low foaming dispersant, especially useful for dispersing inorganic pigments such as titanium dioxide, zinc oxide, clay with improved stability. It is efficient in a wide range of pH in various emulsion systems.

AOPL PS 259 Styrene Acrylic 48%

Chemical type : Styrene Acrylic

Visual Appearance : Milky white

Solid content : 48 +/-2%

Viscosity @ 30 C
Brookfield RVT : 1500 – 2000 cP

Spindale No 7
RPM 20
pH : 8 ~ 10

Free monomer content : < 0.3%

MFFT : 17°C

Properties : Forms a hard, tough, flexible & glossy film. Excellent wet scrub & abrasion resistance. Excellent pigment loading characteristics. Alkali resistant.

Recommended Applications : For use in low cost distemper/interior emulsion paints, cement primer & putty.

AOPL PS 504 Styrene Acrylic 50%

Chemical type : Styrene Acrylic

Visual Appearance : Milky white Viscous Emulsion

Solid content : 50 +/- 1%

Viscosity @ 30 C
Brookfield RVT : 6000 - 8000 cP
Spindale No 4
RPM 10
pH : 8 ~ 9

Free monomer content : < 0.3%

MFFT : 18°C ca

Properties : Forms a hard, tough, flexible & glossy film. Excellent wet scrub & abrasion resistance. Excellent pigment loading characteristics. Alkali resistant.

Recommended Applications : For use in superior quality exterior/interior emulsion paints with high sheen, textured coating & in construction chemicals.

AOPL PS 3045 Styrene Acrylic 45%

Chemical Type : Styrene Acrylic

Visual Appearance : Milky White

Solid Content : 45 +/- 2%

Viscosity @ 30 ºC
Brookfield RVT : 1500 – 2000 cP

Spindale No 4
RPM 10
pH : 8 ~ 10

Free Monomer Content : < 0.3%

MFFT : 18 ºC

Properties : Forms a hard, tough, flexible and glossy film. Excellent wet scrub and abrasion resistant. Excellent pigment loading characteristics, alkali resistant. Can replace 50 % s/a by same volume.

Recommended Applications : For use in low cost washable distemper/ interior emulsion paints /cement primer. Can be use for economical exterior paint

AOPL PVB 55 Vam Acrylate Copolymer

Type : Vam Acrylate Copolymer

Stabilizer : Colloid / Surfactant

Visual Appearance : Milky white

Solids : 55 ± 1 %

Viscosity @ 23 0C
Brookfield RVT : 3500 – 4500 cP
Spindale No 4
RPM 10
Ph : 4 - 5

MFFT : + 7 deg c

Particle Size : 0.2 – 0.3 micron

Film : Medium hard, glossy & non tacky

Applications : Interior flat paint formulations

AOPL PVV 50 VAM VEOVA ter polymer emulsion

AOPL –V50 is a new generation, economical paint binder based on versa tic acid ester terpolymer. It can be used for both interior and exterior paints with good wet scrub resistance and hydrophobicity.

Physical data:

Type : Vinyl Acetate Veova Terpolymer

Visual Appearance : Milky white

Solids : 48-50%

Viscosity @ 23 0C
Brookfield RVT : 2000 - 3000 cP
Spindale No 4
RPM 10

Ph : 6.0-7.0

MFFT : 14 deg c

Film : Clear hard film, free from bits

AOPL V50 can be used for semi gloss paint applications for both interior and exterior paint applications and also for cementitious substrates.

AOPL PVV 55 VAM VEOVA TER POLYMER 55 %

Solid : 55± 1 %

Visual Appearance : Milky white

Viscosity @ 30ºCby
Brookfield RVT : 3000 - 4000 cP
Spindale No 4
RPM 10

MFFT : 12 º C

pH : 4 - 6

Type of Applications : Binder for Interior & exterior emulsion Paints

Characteristics : High Pigment Loading Capacity, Very good wet scrub resistance, Good colour development & superior weatherability

AOPL PT 29 ALKALI SWELLABLE ACRYLIC THICKENER

Introduction AOPL-T29 is a cross linked acrylic co-polymer. Upon addition of a base/alkali the diluted emulsion particles swell. Under these conditions the thickened emulsion clarifies and become highly viscous. These solutions of thickener are similar to solutions of natural gums of higher viscosity grades. The advantage over natural gums is that handling is much simpler as it is in liquid form. Solutions of this thickener suspend pigments and abrasives. AOPL –T29 is ideal for thickening various emulsions used in Textiles, Carpet, Paint and Leather industry.

Technical Data

Visual Appearance : White Milky Emulsion.

Solids : 28.5 % - 29.5 %

pH : 2– 4

Charge : Anionic

Solution Viscosity
1 % Sodium salt : 2000 cP. Minimum.

Salt preparation method: 1 % sodium salt: add 3.3 parts thickener and dilute with 95 parts of water and neutralize with 1.7 parts of 10 % NaOH

Note : 5 % solids level is the maximum concentration for working as above this the viscosity shoots up into an unworkable gel.

AOPL-T29 can readily thicken in the presence of ammonia or other alkali solutions at a ph of 7.5-8.0.

Application

AOPL-T29 can replace natural gums which are difficult to handle.

It is possible to introduce AOPL-T29 directly into the system to be thickened without pre neutralization.
Thickened Solutions of AOPL-T29 can effectively suspend pigments, abrasives and other fine particles.

Advantages

Conventional thickeners have a flocculating action whereas AOPL-T29 does not.

Useful for in situ thickening.

It can also replace partially kerosene usage.

Precautions

Always dilute with water before using.