Textile Industry

ProductTypeVisocityPHDownload Link
AOPL 94Self Thickening Binder20 – 30 cP 3.00Click to Download
AOPL 280Self cross linking PIGMENT BINDER - 7.00 – 7.50Click to Download
AOPL 540Self cross linking extra soft/extra fast Binder4000 – 5000 cP7.00 – 7.50Click to Download
AOPL 4000Self cross linking extra soft5000 – 8000 cP7.00 – 7.50Click to Download
AOPL ABXPoly Vinyl Acetate Emulsion with Internal Plasticizer7000 – 8000 cP 5 to 5.5Click to Download
AOPL APLSelf Thickening Binder8 – 9 cP4.00 – 6.00Click to Download
AOPL EM40Polyvinyl Acetate Emulsion40000 – 50000 cP5 to 5.5Click to Download
AOPL EM50 PPlasticized Homopolymer500 – 700 poise5 to 5.5Click to Download
AOPL EM 50Soft Polyvinyl Acetate50000 – 70000 cP4 to 6Click to Download
AOPL GBAcrylic binder for gold bronze metal powder printing5000 – 8000 cPSlightly alkalineClick to Download
AOPL – Rafix TCationic dye fixing agent for textiles-4.0-6.0Click to Download
AOPL – Raynol rcns TConcentrated Non ionic detergent700 – 1000 cP 12Click to Download
AOPL SANSelf cross linking PIGMENT BINDER20 – 30 cP7.00 – 7.50Click to Download
AOPL SOLSelf cross linking extra soft8000 – 1000 cP7.00 – 7.50Click to Download
AOPL-T 29Alkali Swellable Acrylic Thickener-2– 4Click to Download
Note: The above information is to the best of our knowledge true and accurate. Since the conditions that the products are used in cannot be handled or controlled by us we cannot guarantee the results and assume liability to damages incurred by using this product Refer to M.S.D.S. for handling procedures.

AOPL 94 Self Thickening Binder

Chemical Type : Binder

Description : AOPL 94 is a self cross linking and self thickening acrylic emulsion having durable film properties with excellent thermal and mechanical stability .AOPL 940 is used MAINLY USED IN TABLE PRINTING.

Visual Appearance : Milky white liquid.
Chemical Nature : Acrylic emulsion
Solid Contents : 28 +/- 2%
Viscosity @ 30 C
Brookfield RVT : 20 – 30 cP
Spindale No 3 RPM 10

Emulsifying System : Anionic

pH : 3.00

Storage : Protect from freezing

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL 94 being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing & dry-cleaning. However to increase the rate of cross linking under the normal condition of curing fixer is recommended. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Viscosity of the formulation is dependent upon the equipment and the concentration of ammonia used. Addition of water may be made to adjust the final viscosity. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia. The material is coated, flocked, dried and cured in normal way.

AOPL 280 Self cross linking PIGMENT BINDER

Chemical Type : Binder

Description : AOPL 280 is a self cross linking acrylic emulsion having durable film properties with excellent thermal and mechanical stability. AOPL 280 is used mainly in PIGMENT PRINTING ON CELLULOSIC FABRICS. CAN BE USED IN ZARI,KHADI ETC.

Visual Appearance : Milky white emulsion.

Chemical Nature : Acrylic emulsion

Solid : 40 +/- 2%

Emulsifying System : Nonionic

pH : 7.00 – 7.50

Storage : Protect from freezing

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL 280 being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing and dry-cleaning. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia.

AOPL 540 Self cross linking extra soft/extra fast Binder

Chemical Type : Binder

Description : AOPL 540 is a self cross linking acrylic emulsion having durable film properties with excellent thermal and mechanical stability. AOPL 540 is used mainly in PAERL ,KHADI AND ZARI and WHITE INK.

Visual Appearance : Milky white emulsion.

Chemical Nature : Acrylic emulsion

Solid Contents : 40 +/- 2%

Viscosity @ 30 C
Brookfield RVT : 4000 – 5000 cP
Spindale No 4 RPM 10

Emulsifying System : Nonionic

Ph : 7.00 – 7.50

Storage : Protect from freezing

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL 540 being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing and dry-cleaning. However to increase the rate of cross linking under the normal condition of curing fixer is recommended. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Addition of water may be made to adjust the final viscosity. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia.

AOPL 4000 Self cross linking extra soft

Chemical Type : Binder

Description : AOPL 4000 is a self cross linking acrylic emulsion having durable film properties with excellent thermal and mechanical stability. AOPL 400 is used mainly in PIGMENT PRINTING ON SYNTHATIC FABRICS. CAN BE USED IN ZARI,KHADI ETC

Appearance : Milky white emulsion

Chemical Nature : Acrylic emulsion

Solid Contents : 32 +/- 2%

Viscosity @ 30 C
Brookfield RVT
Spindale No 4 : 5000 – 8000 cP

Speed RPM 10

Emulsifying System : Nonionic

Ph : 7.00 – 7.50

Storage : Protect from freezing

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL 4000 being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing and dry-cleaning. However to increase the rate of cross linking under the normal condition of curing fixer is recommended. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Addition of water may be made to adjust the final viscosity. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia.

AOPL ABX Poly Vinyl Acetate Emulsion with Internal Plasticizer

Chemical type : PVA Emulsion

Description : AOPL ABX is a milky white internally plasticized poly vinyl acetate dispersion which imports a soft handle on textiles and ensures full light fastness and non yellowing properties on the treated fabrics retaining their luster. It is used for durable finishes for cotton, linen, polyester, rayon and various blends.

Visual Appearance : Milky white viscous paste

Solid : 55+/- 1%

Viscosity @ 30ºCby
Brookfield RVT : 7000 – 8000 cP
Spindale No 7 RPM 20

pH of 1% dispersion : 5 to 5.5

Nature : Non-ionic

Stability : Stable to hard water, weak acids and alkalis

Compatibility : Goods pigments and many thermo setting resin

Plasticizer : 12%

Application : For textile finishing and printing.

AOPL APL Self Thickening Binder

Chemical Type : ACRYLIC EMULSION

Description : AOPL APL is a self cross linking and self thickening acrylic emulsion having durable film properties with excellent thermal and mechanical stability. AOPL APL is used mainly in PEARL, KHADI AND ZARI

Visual Appearance : Milky white liquid

Chemical Nature : Acrylic emulsion

Solid Contents : 30 +/- 2%

Viscosity @ 30 C : 8 – 9 cP
Brookfield RVT/ Spindale No 2 / Speed RPM 10

Emulsifying System : Anionic

Ph : 4.00 – 6.00

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL APL being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing and dry-cleaning. However to increase the rate of cross linking under the normal condition of curing fixer is recommended. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Viscosity of the formulation is dependent upon the equipment and the concentration of ammonia used. Addition of water may be made to adjust the final viscosity. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia.

AOPL EM40 Polyvinyl Acetate Emulsion

Chemical Type : PVA Emulsion

Description : AOPL EM40 is a milky white poly vinyl acetate dispersion which imports a firm handle on textiles and ensures full light fastness and non yellowing properties on the treated fabrics retaining their luster. It is used for durable finishes for cotton, linen, polyester, rayon and various blends.

Visual Appearance : Milky white viscous paste.

Solid Content : 40 +/- 2%

Viscosity @ 30ºCby
Brookfield RVT : 40000 – 50000 cP
Spindale No 7 RPM 20

pH of 1% Dispersion : 5 to 5.5

Nature of the Chemical : Non Ionic

Stability : Stable to hard water, weak acids and alkalis

Compatibility : Good pigments and many thermo setting resin

Application : For textile finishing and printing.

AOPL EM50 P PLASTICIZED HOMOPOLYMER

Product Description : Poly Vinyl Acetate Emulsion with Plasticizer

Chemical type : PVA Emulsion

Description : AOPL EM50 P is a milky white poly vinyl acetate dispersion which imports a soft handle on textiles and ensures full light fastness and non yellowing properties on the treated fabrics retaining their luster. It is used for durable finishes for cotton, linen, polyester, rayon and various blends.

Visual Appearance : Milky white viscous paste

Solid content : 50 +/- 1%

Viscosity @ 30ºCby
Brookfield RVT : 500 – 700 poise

Spindale No 7 RPM 20

pH of 1% dispersion : 5 to 5.5

Nature : Non-ionic

Stability : Stable to hard water, weak acids and alkalis

Compatibility : Good pigments and many thermo setting resin

Plasticizer : 2%

AOPL EM 50 SOFT POLYVINYL ACETATE

Product Description : Poly Vinyl Acetate Emulsion

Chemical type : PVA Emulsion

Description : AOPL EM50 is a milky white poly vinyl acetate dispersion which imports a soft handle on textiles and ensures full light fastness and non yellowing properties on the treated fabrics retaining their luster. It is used for durable finishes for cotton, linen, polyester, rayon and various blends.

Visual Appearance : Milky white viscous paste

Solid content : 50 +/-1%

Viscosity @ 30ºCby
Brookfield RVT : 50000 – 70000 cP
Spindale No 7 RPM 20

pH of 1% dispersion : 4 to 6

Nature : Non-ionic

Stability : Stable to hard water, weak acids and alkalis

Compatibility : Good pigments and many thermo setting resin

Application : For textile finishing and printing.

AOPL GB Acrylic binder for gold bronze metal powder printing

Chemical Type : Specialized acrylic emulsion

Visual Appearance : Viscous Milky White paste

Emulsifying system : Non ionic

Viscosity @ 30ºCby
Brookfield RVT : 5000 – 8000 cP

Spindale No 4 RPM 20

pH : Slightly alkaline

Guideline recipe : Gold bronze powder 18 – 22 %

AOPL GB 82 – 76 % Add fixer at time of printing only. Print – dry – cure at 140 c for 5 min.

Precautions :

  • Print paste must not be allowed to become acidic.
  • Printing paste should be used immediately.
  • After printing cloth must be dried without delay.
  • Resin finish after gold printing should be avoided.
  • Presence of discharging agent cause dulling of gold print.
  • To increase viscosity of past natural thickeners like CMC should be used.

AOPL – Rafix T Cationic dye fixing agent for textiles

AOPL –RAFIX T is a cationic fixing agent for reactive and direct dyes. The usage of this helps in fixation and wet fastness of dyed fabrics.

Physical data:

Type : Proprietary fixing chemical

Visual Appearance : Colorless liquid

Solids : 50-52%

pH : 4.0-6.0

charge : Cationic

Solubility : Easily soluble in water

Stability : Stable to acids.

AOPL-RAFIX T has strong and powerful fixation properties at lower dosages than the conventional products. It removes the unevenness of color and the migration problems. When RAMAZOL dyed fabric is required for printing the use of AOPL -RAFIX T helps in strong fixation of the RAMAZOL colors

AOPL – Raynol rcns T Concentrated Non ionic detergent

AOPL –RAYNOL RCNS T is a multipurpose concentrated scouring. / Nonionic detergent with excellent wetting, dispersing and emulsifying properties1

Physical data:

Type : Proprietary detergent formulation

Visual Appearance : Transparent pale yellow viscous liquid

Viscosity @ 30ºCby
Brookfield RVT : 700 – 1000 cP

Spindale No 4 RPM 20

pH : 12

Charge : Nonioinc

Solubility : Easily soluble in water

Stability : Compatible with cationic, anionic and alkaline products

Description: AOPL-RAYNOL RCNS T is a scouring agent for bleaching of cellulose fabrics and their blends . Dosage is about 0.14-0.16% of fabric used. It is used in washing off process to remove unfixed, hydrolyzed dyes and hold them efficiently without redeposition. This results in excellent prints with white back ground.

AOPL SAN Self cross linking PIGMENT BINDER

Chemical Type : Binder

Description : AOPL SAN is a self cross linking acrylic emulsion having durable film properties with excellent thermal and mechanical stability. AOPL SAN is used mainly in PIGMENT PRINTING ON CELLULOSIC FABRICS. CAN BE USED IN ZARI,KHADI ETC.

Visual Appearance : Milky white emulsion.

Chemical Nature : Acrylic emulsion

Solid Contents : 30 +/- 2%

Viscosity @ 30ºCby
Brookfield RVT : 20 – 30 cP

Spindale No 3 RPM 10

Emulsifying System : Nonionic

pH : 7.00 – 7.50

Storage : Protect from freezing

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL SAN being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing and dry-cleaning. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia.

AOPL SOL Self cross linking extra soft

Chemical Type : Binder

Description : AOPL SOL is a self cross linking acrylic emulsion having durable film properties with excellent thermal and mechanical stability. AOPL SOL is used mainly in PIGMENT PRINTING ON HOSIERY FABRICS & also used as water based CLEAR PLASITSOL.

Visual Appearance : Milky white emulsion.

Chemical Nature : Acrylic emulsion

Solid Contents : 40 +/- 2%

Viscosity @ 30ºCby
Brookfield RVT : 8000 – 1000 cP

Spindale No 7 RPM 20

Emulsifying System : Nonionic

pH : 7.00 – 7.50

Storage : Protect from freezing

Curing Temperature : 150 Deg. C with catalyst

Curing Time : 5 to 7 mins

Uses : AOPL SOL being a self cross linking acrylic emulsion catalyst is not needed to achieve durability to washing and dry-cleaning. However to increase the rate of cross linking under the normal condition of curing fixer is recommended. Addition of 1-2% fixer may be necessary to ensure higher wash resistance. Addition of water may be made to adjust the final viscosity. Addition of fixer should be made after adjusting pH 8 - 8.5 by Ammonia.

AOPL-T 29 ALKALI SWELLABLE ACRYLIC THICKENER

Introduction

AOPL-T29 is a cross linked acrylic co-polymer. Upon addition of a base/alkali the diluted emulsion particles swell. Under these conditions the thickened emulsion clarifies and become highly viscous. These solutions of thickener are similar to solutions of natural gums of higher viscosity grades. The advantage over natural gums is that handling is much simpler as it is in liquid form. Solutions of this thickener suspend pigments and abrasives. AOPL –T29 is ideal for thickening various emulsions used in Textiles, Carpet, Paint and Leather industry.

Technical Data

Appearance : White Milky Emulsion.

Solids : 28.5 % - 29.5 %

pH : 2– 4

Charge : Anionic

Solution Viscosity
1 % Sodium salt : 2000 cps. Minimum.

Salt preparation method: 1 % sodium salt: add 3.3 parts thickener and dilute with 95 parts of water and neutralize with 1.7 parts of 10 % NaOH

Note : 5 % solids level is the maximum concentration for working as above this the viscosity shoots up into an unworkable gel.

AOPL-T29 can readily thicken in the presence of ammonia or other alkali solutions at a ph of 7.5-8.0.

Application

AOPL-T29 can replace natural gums which are difficult to handle.

It is possible to introduce AOPL-T29 directly into the system to be thickened without pre neutralization.

Thickened Solutions of AOPL-T29 can effectively suspend pigments, abrasives and other fine particles.
Advantages

Conventional thickeners have a flocculating action whereas AOPL-T29 does not.
Useful for in situ thickening.

It can also replace partially kerosene usage.
Precautions

Always dilute with water before using.

Theme Colors
Layout Style
Background Pattern